KARAKTERISTIK TEGANGAN TEMBUS AC PADA MATERIAL ISOLASI PADAT CAMPURAN EPOXY RESIN DENGAN TONGKOL JAGUNG

Arfan Saputra Arfan Saputra; Lanto Mohammad Kamil Amali

doi:10.54757/fs.v12i1.131

Authors

Arfan Saputra Arfan Saputra Universitas Negeri Gorontalo
Lanto Mohammad Kamil Amali

DOI:

https://doi.org/10.54757/fs.v12i1.131

Keywords:

Tegangan Tembus, Epoxy Resin, Tongkol Jagung, Silika

Abstract

Abstrak – The development of insulation in electric power systems meets the optimal level of reliability. This phenomenon is a challenge in finding new materials to isolate electricity use. One of the insulating materials being developed is an epoxy resin polymer material. This study aims to describe the characteristics of epoxy resin composites added with corncob ash filler as a high-voltage insulation material. The cob ash filler, which is known to contain silica resistant to high temperatures, has good inhibition and can increase mechanical strength. This study was conducted using a direct experimental method in which the isolation of epoxy resin was mixed with corncob ash filler with a mixed variation of 0.5 g, 1 g, 1.5 g, and 2 g. The results show that the more corncob ash filler in the epoxy resin, the faster the failure to penetrate the insulating material made. The breakdown voltage value is 21.64kV on pure epoxy resin insulation material, 10.28kV on a mixture of 0.5 gram corncob ash filler and epoxy resin, 8.93kV on a mixture of 1 gram corncob ash filler and epoxy resin, 7,81kV on a mixture of 1,5 grams corncob ash filler and epoxy resin, and 7,26kV on a mixture of 2 gram corncob ash filler and epoxy resin.

References

Asy’ari H, Budiman A. (2009). Pengaruh Polutan Industri Terhadap Sifat Elektrik dan Sifat Hidrofobik Bahan Isolasi Resin Epoksi Berpengisi Arang Sekam Padi dan Silicone Rubber. UMS, Surakarta.

Dermawan, T. (2012). Pengaruh Komposisi Resin Terhadap Sifat Elektrik Dan Mekanik Untuk Bahan Isolasi Tegangan Tinggi. Yogyakarta: Sekolah Tinggi Teknologi Nuklir.

Erviana L. (2013). Isolasi Silika Dari Tongkol Jagung. Surabaya : Universitas Pembangunan NasionalVeteran Jawa Timur

Fitriah, T. A. (2017). Pengaruh Bahan (Filter) Eceng Gondok dan Sekam Padi pada Material Isolasi Listrik (Polymer Epoxy). Makassar: Program Studi Teknik Elektro Program Pasca Sarjana Universitas Hasanudin Makassar.

Juliandhy, T. (2014). Efek Kegagalan Alat Flue Gas Desulphur Terhadap Tegangan Lewat Denyar Isolasi di Gardu Induk Pembangkitan Tanjung Jati B Jepara. Yogyakarta: Jurnal Nasional Teknik Elektro.

Nadjeeb's. (2009). Dipetik September Sabtu, 2020, dari https://nadjeeb.wordpress.com/resin/

Prasetyo M, Solechan. (2012). Pemanfaatan Batu Bersilika, Silane, dan Vinyl Silane Sebagai Pengisi Bahan Isolasi Resin Epoksi Untuk Isolasi Listrik. Fakultas Teknik Universitas Muhammadiyah Semarang, Semarang.

Pesa, Y. H., & Murdiya, F. (2017). Karakteristik Tegangan Tembus AC pada Material Isolasi Padat Campuran Epoxy Resin dengan Cangkang Kepala Sawit. Pekan Baru: Universitas Riau.

Rasyid A, & Frimurdiya. (2017). Karakteristik Tegangan Tembus Ac Pada Material Isolasi Padat Campuran Resin Dengan Alumina (AL2O3).

Rizkyi, I. P., Susatyo, E. B., & Susilaningsih, E. (2016). Aktivasi Arang Tongkol Jagung Menggunakan Hl Sebagai Adsorben ION Cd (II), Indonesia Journal of Chemical Science, 5(2).

Seppanur, B. (2014). Analisis Kegagalan Isolasi Akibat Patial Discharge pada Kabel Na2xseby 20 KV Berisolasi XLPE dan PVC. Jurnal MomentumTeknik Elektro Vol. 16 No 2.

Yahendra, R. H. (2018). Kajian dan Pengujian Campuran Silika Organik dan Resin Sebagai Bahan Isolasi Listrik. Yogyakarta: Universitas Islam Indonesia.

Yunus, M. Y. (2010). The Study Of Partial Discharge On XLPE Cables. Vol. 8 No.1